Playing with fire

Bead making season is underway at last.  The optimum temperature range for  lamp working glass is between 65 and 80 degrees F, below that range and the glass is too chilled to melt properly, and above that range the artist tends to melt.

Spring and warmer weather arrived long ago but playing in the garden won out, the lawn needed mowing and the vegetable garden had to be planted.  Now with summer here I can finally make time for playing with fire.

Below are a few photos of bead making in progress:  you wrap an initial core of glass onto the steel rod and marver that into a cylinder, then add additional colors on top.  Here I am using a technique to capture a small bubble of air by making a dent in the glass with a sharp steel tool, and then covering the dent with clear glass.

Seattle has a new glass museum, the Chihuly Glasshouse and garden will be an inspiring place to visit.

adding molten glass to the bead

poking dents into the glass

cooling the bead away from the flame

working with flame

How does one make a lampworked glass bead?

half made bead

Take a steel rod of 2 – 3 mm diameter, coated with a clay release agent, and heat up this rod in the flame.  With the other hand, select a glass rod of the color needed, and introduce this slowly to the flame as well.  The end of the glass rod will begin to melt, and form a blob, or “gather.”  Drip this onto the rod, and wrap it around.  Click on the photo for a larger view.

I usually marver the bead now, by rolling it on a flat surface until it takes a cylinder shape, and use this as my canvas to paint with more colors.  I keep adding layers of color, and often finish the bead with some clear glass encasing.

fully molten bead

The bead can be rather lumpy at this point, like a raspberry.   I heat it up further until it is entirely molten, and takes on a smooth rounded shape.  You must continually rotate the rod to keep the bead centered.  If you wish the bead to be textured you skip this rounding.  The bead can also be shaped by rolling it on a flat surface, or pressing it into a mold.

Then let it cool down until the normal colors return to the glass, and put it away in a kiln or warming thermal blanket to rest for several hours.  The next day it can be taken off the rod:   after a soak the clay rinses away and it twists free, the bead is complete and the rod can be re-coated with clay for the next dance.

The flame is a Minor lampworking torch with a mixture of propane and oxygen fuel.  Proper ventilation and didymium safety glasses are essential.  Wikipedia has several good entries relating to beadmaking and glass art.

Click on any photo here for a larger view.

torch, glass rods, and safety glasses